Non-Magnetic Stainless Steels

SUS304, a representative austenitic stainless steel, is nonmagnetic in the solution heat-treated state, but it becomes magnetic due to martensitic transformation after cold working.Therefore, there were challenges such as keeping the processing rate low and sacrificing strength in order to maintain non-magnetic properties.

As Non-magnetic stainless steels are grades that are adjusted so that martensite is not induced (or is not easily induced) by cold working, it can maintain its nonmagnetic properties even after machining. We will propose steel grades according to your usage conditions, such as processing method and required non-magnetic level.

TNM-1 | Non-Magnetic Stainless Steel

MOQ : 100 Kilograms

Application
Other

Chemical Composition
Refer to the image

Grade
TNM-1

Shape
Other, Coil, Sheet

Surface
Bright, Dull

Temper
BA (Bright Annealed), 2B (Skin Passed), As Rolled (Hard)

Thickness
0.010 to 2.0 Millimeter (mm)

Width
3.0 to 300 Millimeter (mm)

Know more

TOKKIN 305M - UNS S30500 | Non-Magnetic Stainless Steel

MOQ : 100 Kilograms

Application
Other, Camera Modules and Components, Communication Equipment Parts, Medical Equipment, Indwelling Needles, Motor Parts *Particularly suitable for applications where magnetism must be minimized.

Chemical Composition
Refer to the image

Grade
TOKKIN 305M

Shape
Coil, Sheet

Surface
Bright, Dull

Temper
BA (Bright Annealed), 2B (Skin Passed), As Rolled (Hard)

Thickness
0.010 to 1.5 mm Millimeter (mm)

Width
3.0 to 300 Millimeter (mm)

Know more